Please be aware that this product can only be shipped to the following countries: Austria, Germany, Switzerland, Belgium, Bulgaria, Croatia, Czech Republic, Denmark, France, Greece, Hungary, Italy, Luxembourg, Netherlands, Norway, Poland, Portugal, Romania, Serbia, Slovakia, Slovenia, Spain, and the United Kingdom,Ireland!
KDSV-10 is a pourable, condensation curing 2-component silicone rubber with low viscosity.
Very soft, for models with strong undercuts.
- Excellent flowability
- Easy processing
- Very good tear resistance
Standard:- Mixing ratio: 100 : 2 parts by weight component A : component B
- Processing time: 50 minutes
- Curing time (HR 25 °C): 4-5 h
Alternatives:- Mixing ratios from 100 : 2 up to 100 : 3
- Processing time (100 g in a cup at 25 °C):
- 100 : 2 = approx. 50 minutes
- 100 : 3 = approx. 30 minutes
- Colour: White
- Mixing viscosity: 13.000 ± 2.000 mPa·s
- Shore A hardness: 10 ± 2
- Tensile strength: > 2.4 N/mm²
- Elongation at break: > 640 %
- Tear resistance strength: > 13 N/mm
- Linear shrinkage (after 7 days): <= 0.3 %
No heat of reaction occurs during vulcanization, so that even larger quantities (e.g. 10 kg) can be poured without the risk of overheating.
Customer information:The release agent Semiperm™ Monofilm in combination with PARTALL® Coverall Film PVA is suitable as a safe release agent for silicone moulds. This combination of release agents provides a barrier layer so that casting with epoxy resins is also possible without any problems. The service life (durability) of the moulds is significantly extended.
The release agent Semiperm™ Monofilm is applied with a brush. After flash-off, PARTALL® Coverall Film PVA is applied, also with a brush or sponge. For more information on processing, see the release agents.
PARTALL® Coverall Film PVA is transferred to the casting, washed off with water after demolding and reapplied before each impression.