R&G Laminating & casting ceramic,bucket 10kg
Product number:
14407
Manufacturer number:
1153153
€105.90*
Content:
10 kg
(€10.59* / 1 kg)
Not in stock. Available only by special order in approx. 7 to 21 business days.
| Quantity / Length in meters: | 10 kg |
|---|---|
| Content sufficient for: | 5,6 L Gieß oder 6,5 L Laminierkera |
| Gefahrenhinweise: | H315, H318 |
| Sicherheitshinweise: | P310, P305, P351, P338 |
| Piktogramme: | GHS05 |
Low-viscosity, water-bound synthetic gypsum for casting and laminating.
Specific advantages:
Laminating ceramic:
In conjunction with M1 Glass mat complex 600 g/m² as reinforcement and R&G mould resin as tooling coat.
Suitable for all mould sizes (conventional sizes range from postcard formats to 15 m²)
Mixing ratio:
(for 1 m² M1 Glass mat complex 600 g/m² the consumption is 8.5 kg powder + 2.38 l water )
Casting ceramic:
(Attention: colder water extends this time, warm water accelerates)
Caution:
If metals are introduced into the plaster mould to reinforce the mould, reactions with the laminating and casting ceramics may occur. If possible, do not use aluminium for this.
The casting compound deaerates quite well and results in hard moulded parts which can be easily processed, e.g. by grinding, sawing and milling. Painting with commercial colours, almost everything is suitable here.
Laminating and cast ceramic shows a surface condition and hardness similar to marble.
Also suitable for casting of figurines and reliefs.
Please note:
Laminating ceramic is a plaster-based moulding compound, which exhibits no permanent resistance to water. If outdoor exposure is inevitable, it should be coated with an appropriate paint system such as PU paints beforehand.
Specific advantages:
- High dimensional accuracy
- High bending tensile strength in conjunction with M1 Glass mat complex 600 g/m²
- Ease of processing
- Fast curing without the addition of accelerators
- The porcelain-like appearance of cured parts
- No drying or firing necessary
- High reproduction accuracy•Surface design possible with all common paints and lacquers
- Physiologically safe
Laminating ceramic:
In conjunction with M1 Glass mat complex 600 g/m² as reinforcement and R&G mould resin as tooling coat.
Suitable for all mould sizes (conventional sizes range from postcard formats to 15 m²)
Mixing ratio:
- 1 kg powder to 280 ml of water yields 0.6 l moulding compound
(for 1 m² M1 Glass mat complex 600 g/m² the consumption is 8.5 kg powder + 2.38 l water )
- Processing time: 15-35 minutes
- Solidification point: 50 minutes
- Resistant: Up to 150 ° C (operating temperature depends on the used epoxy system)
- Fully loadable: After 3-4 hours
- Colour: Ivory
- Hardeness Shore D: > 90
Casting ceramic:
- Mixing ratio: 1 kg powder: 190 ml of water
- Mixing volume of 4 kg powder and 1l water: 2.5 - 2.6l
- Processing time: Approx. 35 - 45 minutes
(Attention: colder water extends this time, warm water accelerates)
- End of solidification: Approx. 50 - 60 minutes
Caution:
If metals are introduced into the plaster mould to reinforce the mould, reactions with the laminating and casting ceramics may occur. If possible, do not use aluminium for this.
The casting compound deaerates quite well and results in hard moulded parts which can be easily processed, e.g. by grinding, sawing and milling. Painting with commercial colours, almost everything is suitable here.
Laminating and cast ceramic shows a surface condition and hardness similar to marble.
Also suitable for casting of figurines and reliefs.
Please note:
Laminating ceramic is a plaster-based moulding compound, which exhibits no permanent resistance to water. If outdoor exposure is inevitable, it should be coated with an appropriate paint system such as PU paints beforehand.
Manufacturer and responsible person (information obligations under the GPSR Product Safety Regulation)